PA11 BECNOTL - Cable Coating
Price:150
Other Products
Description
Additional Information
Rilsan® BECNO TL resin is a polyamide produced from renewable resources. This natural grade is specifically designed for cable coating. The bio-based content percentage is >98% as calculated per ASTM D 6866.
Rilsan® BECNO TLMain Applications:Wire and cable sheathing.
Rilsan® BECNO TL Packaging:This grade is delivered dry in sealed packaging (25 kg bags), ready for processing.
PA11 BECNOTL Technical Parameters
| Physical Properties | Value/Unit | Test Standard | Test Condition |
|---|---|---|---|
Density | 1.03 g/cm³ | ISO 1183 | Cond. |
Density | 1.03 g/cm³ | ISO 1183 | Dry |
Melt Volume-Flow Rate (MVR) | |||
235℃/2.16 kg | 30 cm³/10 min | ISO 1133 | Dry |
Water Absorption | 1.9 % | ISO 62 | Dry |
Bio-based Content | 98 % | ASTM 6866 | |
| Mechanical Properties | Value/Unit | Test Standard | Test Condition |
Tensile Strength | |||
Yield (yld) | 42 MPa | ISO 527-1/-2 | Cond. |
Yield (yld) | 43 MPa | ISO 527-1/-2 | Dry |
Tensile Elongation | |||
Yield (yld) | 5 % | ISO 527-1/-2 | Cond. |
Yield (yld) | 5 % | ISO 527-1/-2 | Dry |
Nominal Elongation at Break | 50 % | ISO 527-1/-2 | Cond. |
Nominal Elongation at Break | 50 % | ISO 527-1/-2 | Dry |
Tensile Modulus | 1330 MPa | ISO 527-1/-2 | Cond. |
Tensile Modulus | 1470 MPa | ISO 527-1/-2 | Dry |
Puncture Performance | |||
Force | 5500 N | ISO 6603-2 | Cond., -30°C |
Energy | 65 J | ISO 6603-2 | Cond., -30°C |
| Impact Properties | Value/Unit | Test Standard | Test Condition |
Charpy Notched Impact Strength | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | 9 kJ/m² | ISO 179/1eA | Cond. |
Charpy Unnotched Impact Strength | |||
-30℃ (-22℉) | kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) | kJ/m² | ISO 179/1eU | Cond. |
| Thermal Properties | Value/Unit | Test Standard | Test Condition |
Heat Deflection Temperature (HDT) | |||
0.45 MPa (66 psi) (4.6 kg/cm²) | 150 °C | ISO 75-1/-2 | Dry |
1.8 MPa (264 psi) (18.6 kg/cm²) | 55 °C | ISO 75-1/-2 | Dry |
Vicat Softening Temperature | 160 °C | ISO 306 | Dry, 50°C/h 50N |
Coefficient of Linear Thermal Expansion (CLTE) | |||
Longitudinal (Flow) | 90 E-6/K | ISO 11359-1/-2 | Dry |
Melting Temperature (Tm) | 189 °C | ISO 11357-1/-3 | Dry, 10°C/min |
Processing Temperature | 270 °C | - | Injection Molding |
Mold Temperature | 50 °C | - | Injection Molding |
| Flammability Properties | Value/Unit | Test Standard | Test Condition |
UL Flammability Rating | |||
V-2 | 1.6 mm | IEC 60695-11-10 | Dry |
V-2 | 3.2 mm | IEC 60695-11-10 | Dry |
Oxygen Index (LOI) | 25 % | ISO 4589-1/-2 | Dry |
| Electrical Properties | Value/Unit | Test Standard | Test Condition |
Volume Resistivity | 1.0E+12 Ohm·m | IEC 60093 | Cond. |
Surface Resistivity | 1.0E+14 Ohm | IEC 60093 | Cond. |
Dielectric Constant (DK) | |||
100Hz | 3 - | IEC 60250 | Dry |
1MHz | 3 - | IEC 60250 | Dry |
Dissipation Factor (DF) | |||
100Hz | 274 E-4 | IEC 60250 | Dry |
1MHz | 166 E-4 | IEC 60250 | Dry |
Comparative Tracking Index (CTI) | |||
- | 600 - | IEC 60112 | Cond. |
Dielectric Strength | 30 kV/mm | IEC 60243-1 | Cond. |